Stat-Tech™ Compound combines polypropylene with anti-static additives.
| Original Document | Technical Datasheet(English) | |||
| Features | Anti-Static | |||
| Additive | Antistatic Additive | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Compliance | RoHS | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
230°C/3.8 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | |
Across Flow | ***~*** % | ASTM D955 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | Type I, 5.1 mm/min |
Tensile Strength | |||
Break | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 5.1 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | 3.18 mm, Injection Molded |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 6.35 mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 6.35 mm |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | ***~*** Ohm-cm | ASTM D257 | 3.18 mm |
Surface Resistivity | ***~*** Ohm | ASTM D257 | 3.18 mm |
Static Decay | *** seconds | MIL B-81705C | 12% RH, 5000 kV to 50 kV |
Static Decay | *** seconds | MIL B-81705C | 50% RH, 5000 kV to 50 kV |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.