Maxxam™ FR flame-retardant polyolefin compounds and masterbatches meet stringent flammability performance requirements defined by industry agencies, including Underwriters Laboratories UL 94 V-2, V-0, and 5VA performance ratings. In addition, many compounds in the Maxxam FR portfolio offer elevated Relative Thermal Index (RTI) ratings.
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantHomopolymer | |||
| Additive | Flame Retardant | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
230°C/2.16 kg | *** g/10min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 51 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 51 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | |
Poisson Ratio | *** - | ASTM D 638 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | 3.18 mm, Injection Molded |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Unannealed, 3.18 mm |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | NC and Black |
V-0 | *** mm | UL94 | NC and Black |
V-0 | *** mm | UL94 | NC and Black |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | |
1.5mm | *** °C | IEC 60695-2-12 | |
3mm | *** °C | IEC 60695-2-12 | |
Glow Wire Ignition Test(GWIT) | |||
0.75mm | *** °C | IEC 60695-2-13 | |
1.5mm | *** °C | IEC 60695-2-13 | |
3.0mm | *** °C | IEC 60695-2-13 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
- | PLC | UL 746 | |
Dielectric Strength | *** kV/mm | ASTM D149 | |
High Voltage Arc Tracking Rate(HVTR) | PLC | UL 746 | |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | 0.75 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | 1.5 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | 3.0 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | 0.75 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | 1.5 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | 3.0 mm |
High Voltage Arc Resistance to Ignition(HVAR) | *** PLC | UL 746 | 0.75 mm |
High Voltage Arc Resistance to Ignition(HVAR) | *** PLC | UL 746 | 1.5 mm |
High Voltage Arc Resistance to Ignition(HVAR) | *** PLC | UL 746 | 3.0 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.