Glass Fiber Reinforced, PTFE lubricated, Impact Modified, Flame Retardant Polycarbonate Compound
| Original Document | Technical Datasheet(English) | |||
| Features | Toughened/Impact ModifiedFlame RetardantWear/Abrasion ResistanceLow Friction/WearFilled & Reinforced | |||
| Additive | Flame RetardantImpact ModifierLubricant | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 20% Glass Fiber15% PTFE35% Glass Fiber+PTFE | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
Flow | ***~*** % | ASTM D955 | 3.00 mm |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ASTM D 638 | 5.0 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | 5.0 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | 1.3 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | 3.20 mm, Injection Molded |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Unannealed |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Surface Resistivity | *** Ohm | ASTM D257 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.