Crastin® HR5330HF is a 30% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resistance. Developed for USCAR Class 3 and 4 environments.
| Original Document | Technical Datasheet-ISO(Chinese) | |||
| Features | Good ToughnessHydrolysis ResistanceHigh FlowFilled & Reinforced | |||
| Compliance | USCAR | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** kg/m³ | ISO 1183 | |
Melt Volume Flow Rate(MVR) | |||
250℃/2.16 kg | *** cm³/10 min | ISO 1133 | |
Molding Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | |
Across Flow | *** % | ISO 294-4, 2577 | |
Water Absorption | *** % | ISO 62 | 2mm |
Moisture /Humidity Absorption | *** % | ISO 62 | 2mm |
Viscosity | *** cm³/g | ISO 307, 1157, 1628 | |
Melt Density | *** kg/m³ | - | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
Poisson Ratio | *** - | ISO 527-1/-2 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50℃/h 50N |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746B | |
Specific Heat | *** J/kg-K | - | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | |
Flow | *** E-6/K | ISO 11359-1/-2 | -40-23℃ |
Flow | *** E-6/K | ISO 11359-1/-2 | 55-160℃ |
Across Flow | *** E-6/K | ISO 11359-1/-2 | |
Across Flow | *** E-6/K | ISO 11359-1/-2 | -40-23℃ |
Across Flow | *** E-6/K | ISO 11359-1/-2 | 55-160℃ |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10℃/min |
Glass Transition Temperature | *** °C | ISO 11357-1/-2 | 10℃/min |
Thermal Conductivity | *** W/(m K) | - | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589-1/-2 | |
Glow Wire Flammability Index(GWFI) | |||
3mm | *** °C | IEC 60695-2-12 | |
FMVSS | *** - | FMVSS 302 | |
Burning Rate | *** mm/min | ISO 3795 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
100Hz | *** E-4 | ASTM D 150 | |
100Hz | *** E-4 | IEC 60250 | |
1 kHz | *** E-4 | ASTM D 150 | |
1MHz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | ASTM D150 | |
Comparative Tracking Index (CTI) | |||
- | *** - | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | Short Time, 1mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.