| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Density/Specific Gravity |
*** g/cm³
| DIN 53479 | |
K-Value |
***~*** -
| - | 96% H2SO4 |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus |
*** Mpa
| ISO 527-2 | 23°C, 1 mm/min |
Tensile Strength | | | |
Break |
*** Mpa | ISO 527-2/5 | 23°C |
Tensile Elongation | | | |
Break |
*** % | ISO 527-2/5 | 23°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 179/1eA | |
23℃ (73℉) |
*** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | | | |
-30℃ (-22℉) |
*** kJ/m² | ISO 179 | |
23℃ (73℉) |
*** kJ/m² | ISO 179 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75-2/B | Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75-2/A | Unannealed |
Relative Temperature Index(RTI), Imp | | | |
0.7mm |
*** °C | UL 746 | |
1.5/1.6 mm |
*** °C | UL 746 | |
3.0/3.2 mm |
*** °C | UL 746 | |
Relative Temperature Index(RTI), Elec | | | |
0.7mm |
*** °C | UL 746 | |
1.5/1.6 mm |
*** °C | UL 746 | |
3.0/3.2 mm |
*** °C | UL 746 | |
Relative Temperature Index(RTI), Str | | | |
0.7mm |
*** °C | UL 746 | |
1.5/1.6 mm |
*** °C | UL 746 | |
3.0/3.2 mm |
*** °C | UL 746 | |
Melt Temperature(Tm) |
*** °C
| ISO 3146 | DSC |
Continuous Use Temperature | | | |
Long term |
*** °C | IEC 60216 | GTP 50% Tensile |
Temperature at Short Circle Operation |
*** °C
| IEC 60216 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | | | |
HB |
*** mm | UL94 | ALL |
HB |
*** mm | UL94 | ALL |
HB |
*** mm | UL94 | ALL |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity |
*** Ohm-cm
| IEC 60093 | |
Surface Resistivity |
*** Ohm
| IEC 60093 | |
Dielectric Constant(Permittivity) | | | |
1MHz |
*** - | IEC 60250 | |
Comparative Tracking Index (CTI) | | | |
- |
PLC | UL 746 | |
Dielectric Strength |
*** kV/mm
| ASTM D149 | |
Arc Resistance |
*** PLC
| ASTM D495 | |
High Voltage Arc Tracking Rate(HVTR) |
PLC
| UL 746 | |
Hot Wire Ignition(HWI) |
*** PLC
| UL 746 | 0.70 mm |
Hot Wire Ignition(HWI) |
*** PLC
| UL 746 | 1.5 mm |
Hot Wire Ignition(HWI) |
PLC
| UL 746 | 3.0 mm |
High Ampere Arc Ignition(HAI) |
PLC
| UL 746 | 0.70 mm |
High Ampere Arc Ignition(HAI) |
PLC
| UL 746 | 1.5 mm |
High Ampere Arc Ignition(HAI) |
PLC
| UL 746 | 3.0 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.