30% glass fiber, exc. bal. of properties
The Standard for the Industry. Excellent balance of properties, including easy flow, easy processing, thermal stability, chemical resistance, mechanical and electrical properties. Suitable for vapor phase surface mount electrical and electronic devices. 30% glass reinforced Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant FDA compliant UL-Listing V-0 in natural and black at 0.2mm thickness per UL 94 flame testing, and UL-5VA in natural at 1.5mm. Relative-Temperature-Index (RTI) according to UL 746B: electricals 240°C, mechanicals 220°C at 0.85mm. UL = Underwriters Laboratories (USA)
| Original Document | Technical Datasheet(English) | |||
| Features | Heat StabilizedFlame RetardantEasy processingUV StabiltiyChemical ResistanceHigh FlowFilled & Reinforced | |||
| Additive | Light StabilizerLight Stabilizer | |||
| Appearance | Pellets/GranulesNatural ColorBlack | |||
| Processing | Injection | |||
| Compliance | FDA | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | |
Across Flow | *** % | ISO 294-4, 2577 | |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C/50%RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23°C |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899-1 | |
1000h | *** Mpa | ISO 899-1 | |
Compressive Modulus | *** Mpa | ISO 604 | |
Compressive Strength | *** Mpa | ISO 604 | at 1% Strain |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50°C/h 50N |
Relative Temperature Index(RTI), Imp | |||
0.85mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.85mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.85mm | *** °C | UL 746B | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-2 | |
Across Flow | *** E-6/°C | ISO 11359-2 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
5VA | *** mm | UL94 | |
Oxygen Index | *** % | ISO 4589-1/-2 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
100Hz | *** - | IEC 60250 | |
1MHz | *** - | IEC 60250 | |
Dissipation Factor | |||
100Hz | *** E-4 | IEC 60250 | |
1MHz | *** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
- | *** - | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243-1 | |
Arc Resistance | *** sec | Company |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.