Color- Black
Norm compliance- Compliant with Regulation (EC) No 1907/2006 (REACh)
Processing technology- Injection moulding
| Original Document | Technical Datasheet(English) | |||
| Appearance | Black | |||
| Processing | Injection | |||
| Compliance | REACH (EC 1907/2006) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
220℃/10 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
- | *** % | Internal | |
Water Absorption | *** % | ASTM D570 | 24 h/23°C |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Break | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | 50°C/h at 10 N |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | 50°C/h at 50 N |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6/K | ASTM D 696 | |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
1 kHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
1 kHz | *** E-4 | ASTM D 150 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | ASTM D149 | 1.6mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.