Zytel® 79G13HSL NC010 is a 13 % glass reinforced, heat stabilized, lubricated slightly toughened black polyamide 66 for injection molding. It has improved impact resistance.
| Original Document | Technical Datasheet-ISO(Chinese) | |||
| Features | High ImpactGood ToughnessHeat ResistanceHeat StabilizedFilled & Reinforced | |||
| Reinforced | 13% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** kg/m³ | ISO 1183 | |
Molding Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | |
Across Flow | *** % | ISO 294-4, 2577 | |
Water Absorption | *** % | ISO 62 | 2mm |
Moisture /Humidity Absorption | *** % | ISO 62 | 2mm |
Melt Density | *** kg/m³ | - | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | Conditioned |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | |
Break | *** Mpa | ISO 527-1/-2 | Conditioned |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | |
Break | *** % | ISO 527-1/-2 | Conditioned |
Tensile Creep Modulus | |||
1h | *** Mpa | ISO 899-1 | Conditioned |
1000h | *** Mpa | ISO 899-1 | Conditioned |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Conditioned |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Conditioned |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | |
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | Conditioned |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ISO 2039-2 | |
Rockwell M | *** M | ISO 2039-2 | Conditioned |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 50℃/h 50N |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746B | |
1.5/1.6 mm | *** °C | UL 746B | |
3.0/3.2 mm | *** °C | UL 746B | |
Specific Heat | *** J/kg-K | - | |
Specific Heat | *** J/kg-K | - | melt |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/K | ISO 11359-1/-2 | |
Across Flow | *** E-6/K | ISO 11359-1/-2 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10℃/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
HB | *** mm | UL94 | |
FMVSS | *** - | FMVSS 302 | |
Burning Rate | *** mm/min | ISO 3795 | 1mm |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Comparative Tracking Index (CTI) | |||
- | *** - | IEC 60112 | |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Fogging | |||
G-value (condensate) | *** mg | ISO 6452 | |
Volatile Organic Compounds | *** µgC/g | VDA 277 | |
Odor test | *** class | VDA 270 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.