PA66, unfilled, good low temperature impact resistance, high heat aging resistance
Car industry, Household appliances, Electrical devices.
| Original Document | Technical Datasheet(English) | |||
| Features | High Impact at Low TemperaturGood Heat Aging | |||
| Additive | Impact Modifier | |||
| Appearance | Black | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | |
Across Flow | *** % | ISO 294-4, 2577 | |
Water Absorption | *** % | ISO 62 | 23°C-sat |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C/50%RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Dry |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/1A | Dry, 50mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-2/1A | Dry, 50mm/min |
Break | *** % | ISO 527-2/1A | Dry, 50mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 23°C |
Flexural Strength | |||
Break | *** Mpa | ISO 178 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | Dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | Dry |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | |
Continuous Use Temperature | |||
Long term | *** °C | IEC 60216-1 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Dielectric Strength | *** kV/mm | IEC 60243-1 | Dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.