Injection molding grade, reinforced with ca. 26 % glass fibers
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF26 POM copolymer Injection molding type, reinforced with ca 26 % glass fibers; high resistance to thermal and oxidative degradation; reduced thermal expansion and shrinkage. UL-registration for all colours and a thickness more than 1.57 mm as UL 94 HB, temperature index UL 746 B electrical 105 °C, mechanical 95 °C (tensile impact) and 100 °C (tensile). Burning rate ISO 3795 and FMVSS 302 < 100 mm/min and a thickness more than 1 mm thickness. Ranges of applications: For molded parts with very high strength and rigidity as well as higher hardness. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA)
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高挺度耐热耐热老化尺寸稳定抗氧化共聚物填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 26% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.6 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 4 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.6 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1 % | ISO 294-4, 2577 | |
吸水率 | 0.9 % | ISO 62 | 23°C-sat |
吸湿率 | 0.17 % | ISO 62 | 23°C/50%RH |
熔体密度 | 1.35 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 135 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
- | 165 Mpa | ISO 178 | 23°C |
弯曲模量 | 7800 Mpa | ISO 178 | 23°C |
拉伸模量 | 9200 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 7700 Mpa | ISO 899-1 | |
1000h | 5400 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 8 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 35 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 30 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 200 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 160 °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | 125 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 158 °C | ISO 306 | 50°C/h 50N |
比热容 | 1810 J/kg-K | - | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 40 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 80 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |
导热系数 | 0.215 W/(m K) | - | |
热扩散系数 | 6.5E-8 m²/s | - | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3.18 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 4.3 - | IEC 60250 | |
1MHz | 4.3 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 30 E-4 | IEC 60250 | |
1MHz | 60 E-4 | IEC 60250 | |
相对漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | |
绝缘强度 | 40 kV/mm | IEC 60243-1 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。