Injection molding grade, reinforced with ca. 20 % glass fibers
Chemical abbreviation according to ISO 1043-1: POM Molding compound ISO 9988- POM-K, M-GNR, 02-003, GF20 POM copolymer Injection molding type, reinforced with ca. 20 % glass fibers; high resistance to thermal and oxidative degradation; reduced thermal expansion and shrinkage. UL-registration in natural and black and a thickness more than 1.5 mm as UL 94 HB, temperature index UL 746 B, electrical 105 °C, mechanical 105 °C Burning rate ISO 3795 and FMVSS 302 < 100 mm/min for a thickness more than 1 mm thickness. Ranges of applications: For molded parts with high strength and rigidity as well as higher hardness. FMVSS = Federal Motor Vehicle Safety Standard (USA) UL = Underwriters Laboratories (USA)
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性耐热耐热老化尺寸稳定抗氧化共聚物填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.55 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
190℃/2.16 kg | 4.5 cm³/10min | ISO 1133 | |
收缩率 | |||
纵向(Flow) | 0.7 % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.1 % | ISO 294-4, 2577 | |
吸水率 | 0.85 % | ISO 62 | 23°C-sat |
吸湿率 | 0.19 % | ISO 62 | 23°C/50%RH |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 120 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 3 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
断裂(brk) | 170 Mpa | ISO 178 | |
弯曲应变 | |||
断裂(brk) | 3.4 % | ISO 178 | |
弯曲模量 | 6900 Mpa | ISO 178 | 23°C |
拉伸模量 | 7200 Mpa | ISO 527-2/1A | |
拉伸蠕变模量 | |||
1h | 6500 Mpa | ISO 899-1 | |
1000h | 4000 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 8 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 40 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 35 kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
球压硬度 | 190 Mpa | ISO 2039-1 | 30s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 159 °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | 105 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 50 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 80 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 166 °C | ISO 11357-1/-3 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 4.3 - | IEC 60250 | |
1MHz | 4.3 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 30 E-4 | IEC 60250 | |
1MHz | 60 E-4 | IEC 60250 | |
相对漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | |
绝缘强度 | 35 kV/mm | IEC 60243-1 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。