improved fuel resistance including hot diesel, UV resistant
Hostaform® acetal copolymer grade C13031 XF LS 10/1570 is an acetal copolymer modified to resist deterioration from aggressive fuel blends. Additionally the material contains UV stabilizers and carbon black to improve also the UV resistance. This material is specially targeted for transportation industry fuel systems.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 抗紫外线耐燃油共聚物 | |||
| 添加助剂 | 紫外线稳定剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 炭黑 | |||
| 物理性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
|---|---|---|---|---|
密度 | 1.42/ * | g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | ||||
190℃/2.16 kg | 12/ * | cm³/10min | ISO 1133 | |
收缩率 | ||||
纵向(Flow) | 2.2/ * | % | ISO 294-4, 2577 | |
横向(Across Flow) | 1.9/ * | % | ISO 294-4, 2577 | |
吸湿率 | 0.3/ * | % | ISO 62 | 23°C/50%RH |
| 机械性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
拉伸强度 | ||||
屈服(yld) | 60/ * | Mpa | ISO 527-2/1A | 50mm/min |
拉伸延伸率 | ||||
屈服(yld) | 11/ * | % | ISO 527-2/1A | 50mm/min |
标称断裂伸长率 | 30/ * | % | ISO 527-2/1A | 50mm/min |
弯曲强度 | ||||
- | 76/ * | Mpa | ISO 178 | |
弯曲模量 | 2900/ * | Mpa | ISO 178 | 23°C |
拉伸模量 | 2800/ * | Mpa | ISO 527-2/1A | |
| 冲击性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | ||||
-30℃ (-22℉) | 6/ * | kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 7.5/ * | kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | ||||
-30℃ (-22℉) | 140/ * | kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 150/ * | kJ/m² | ISO 179/1eU | |
| 硬度性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 88/ * | M | ISO 2039-2 | |
球压硬度 | 137/ * | Mpa | ISO 2039-1 | 30s |
| 热学性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | ||||
0.45 Mpa (66 psi)（4.6kg/cm²） | 159/ * | °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 102/ * | °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | ||||
纵向(Flow) | 90/ * | E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 90/ * | E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 170/ * | °C | ISO 11357-1/-3 | 10°C/min |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。