50% Mineral/Glass reinforced, low warpage, good surface, V-0
Fortron 6850L6 offers the lowest warpage available. The easy flowing nature allows this product to be injection molded into thin walled applications. The excellent balance of mineral and glass fibers result in a superior heat resistance and dimensional stability. This grade is inherently flame-retardant along with high hardness and rigidity. Especially used for thin walled by unfavorable flow length-wall thickness ratio. This is the most isotropic grade available.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性耐热阻燃良好表面尺寸稳定低翘曲高流动各向同性填充增强 | |||
| 添加助剂 | 脱模剂 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 50% 玻纤+矿物 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.8 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.3~0.6 % | ISO 294-4, 2577 | |
横向(Across Flow) | 0.4~0.6 % | ISO 294-4, 2577 | |
吸水率 | 0.02 % | ISO 62 | 23°C-sat |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 125 Mpa | ISO 527-2/1A | 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 1 % | ISO 527-2/1A | 5mm/min |
弯曲强度 | |||
断裂(brk) | 190 Mpa | ISO 178 | |
弯曲模量 | 16800 Mpa | ISO 178 | 23°C |
拉伸模量 | 18500 Mpa | ISO 527-2/1A | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 4 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 16 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 16 kJ/m² | ISO 179/1eU | |
悬臂梁缺口(Izod Notched) | |||
-30℃ (-22℉) | 4 kJ/m² | ISO 180/1A | |
23℃ (73℉) | 4 kJ/m² | ISO 180/1A | |
悬臂梁无缺口(Izod Unnotched) | |||
-30℃ (-22℉) | 20 kJ/m² | ISO 180/1U | |
23℃ (73℉) | 20 kJ/m² | ISO 180/1U | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 96 M | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 270 °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | 215 °C | ISO 75-1/-2 | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 15 E-6/°C | ISO 11359-2 | |
横向(Across Flow) | 31 E-6/°C | ISO 11359-2 | |
熔融温度(Tm) | 280 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | 90 °C | ISO 11357-1/-2 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 0.38 mm | UL94 | |
V-0 | 1.5 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
耗散因数(DF) | |||
1MHz | 10 E-4 | IEC 60250 | |
绝缘强度 | 25 kV/mm | IEC 60243-1 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。