30% Glass reinforced, excellent flow, good weldability, V-0
Fortron 1130L4 is a 30% glass-reinforced PPS that has excellent heat and chemical resistance. It is inherently flame-retardant and exhibits high hardness and a good balance of strength and stiffness. Especially used for thin walled parts requiring long flow lengths. This grade also exhibits excellent weldability in secondary operations due to its low filler content.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat ResistanceFlame RetardantGood WeldChemical ResistanceHigh FlowFilled & Reinforced | |||
| Additive | Lubricant | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4, 2577 | |
Across Flow | *** % | ISO 294-4, 2577 | |
Water Absorption | *** % | ISO 62 | 23°C-sat |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 23°C |
Flexural Strength | |||
Break | *** Mpa | ISO 178 | |
Compressive Modulus | *** Mpa | ISO 604 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180/1U | |
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-2 | |
Across Flow | *** E-6/°C | ISO 11359-2 | |
Glass Transition Temperature | *** °C | ISO 11357-1/-2 | 10°C/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
V-0 | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Surface Resistivity | *** Ohm | IEC 60093 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.