Polypropylene copolymer reinforced with 20weight percent long glass fibers. Low emission. The fibers are chemically coupled to the polypropylene matrix. The pellets are cylindrical and normally as well as the embedded fibers 10 mm long.(-0553 = Low emission grade)
Parts molded of CELSTRAN have outstanding mechanical properties such as high strength and stiffness combined with high heat deflection. The notched impact strength is increased at elevated and low temperatures due to the fiber skeleton built in the parts. The long fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the warpage.
Complex parts can be manufactured with high reproducibility by injection molding.
Application field: Functionial/structural parts for automotive
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高强度高刚性高冲击耐低温冲击耐热低翘曲抗蠕变填充增强 | |||
| 颜色形状 | 粒状黑色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 20% 长玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.03 g/cm³ | ISO 1183 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 84 Mpa | ISO 527-2/1A | 5mm/min |
- | 60 Mpa | ISO 527-2/1A | 80°C |
拉伸延伸率 | |||
断裂(brk) | 2.5 % | ISO 527-2/1A | 5mm/min |
断裂(brk) | 2.6 % | ISO 527-2/1A | 80°C |
弯曲强度 | |||
- | 140 Mpa | ISO 178 | 23°C |
- | 90 Mpa | ISO 178 | 80°C |
弯曲模量 | 4500 Mpa | ISO 178 | 23°C |
弯曲模量 | 3400 Mpa | ISO 178 | 80°C |
拉伸模量 | 4700 Mpa | ISO 527-2/1A | 1mm/min |
拉伸模量 | 3400 Mpa | ISO 527-2/1A | 80°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 20 kJ/m² | ISO 179/1eA | |
23℃ (73℉) | 20 kJ/m² | ISO 179/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | 60 kJ/m² | ISO 179/1eU | |
23℃ (73℉) | 56 kJ/m² | ISO 179/1eU | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 159 °C | ISO 75-1/-2 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。