Material code according to ISO 1043-1: PP
Polypropylene with 40 weight percent ash content, long
glass fibers reinforced. The fibers are chemically coupled to the polypropylene
matrix. The pellets are cylindrical and normally as well as the
embedded fibers 10 mm long.
Parts molded of CELSTRAN have outstanding mechanical properties such
as high strength and stiffness combined with high heat deflection.
The notched impact strength is increased at elevated and low
temperatures due to the fiber skeleton built in the parts. The long
fiber reinforcement reduces creep significantly.
The very isotropic shrinkage in the molded parts minimizes the
warpage.
Complex parts can be manufactured with high reproducibility by
injection molding.
Application field: Functional/structural parts for automotive
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat ResistanceLow WarpageCreep ResistantFast Cycle TimeFilled & Reinforced | |||
| Processing | Injection | |||
| Reinforced | 40% Long Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | 1mm/min |
Tensile Modulus | *** Mpa | ISO 527-2/1A | 80°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | 5mm/min |
- | *** Mpa | ISO 527-2/1A | 80°C |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | 5mm/min |
Break | *** % | ISO 527-2/1A | 80°C |
Flexural Modulus | *** Mpa | ISO 178 | 23°C |
Flexural Modulus | *** Mpa | ISO 178 | 80°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 23°C |
- | *** Mpa | ISO 178 | 80°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
8 Mpa (1160 psi)（81.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.