PA66 injection moulding grade. Toughened, heat stabilized. Black colour.
Suitable for parts requiring good impact resistance and improved surface appearance. Good properties retention after ageing.
ISO 1043 : PA66-IT
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactGood ToughnessHeat StabilizedGood Heat AgingGood Surface | |||
| Additive | FlexibilizerHeat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Compliance | RoHS | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294-4 | |
Across Flow | ***~*** % | ISO 294-4 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/1A | Dry, 50mm/min |
Tensile Elongation | |||
Yield | *** % | ISO 527-2/1A | Dry, 50mm/min |
Nominal Tensile Strain at Break | *** % | ISO 527-2/1A | Dry, 50mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry, 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 179/1eA | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/Bf | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.