PA610 60% glass fiber reinforced injection moulding grade. Heat stabilized. Black colour.
Suitable for parts requiring very high stiffness and good mechanical resistance. Used in drinking water applications.
This grade is partially renewably-sourced (60% of base polymer by weight).
ISO 1043 : PA610-T GF60
| Original Document | Technical Datasheet(English) | |||
| Features | High Stiffness/RigidityHeat StabilizedBio-basedRenewable ResourceDrinking Water ContactFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Black | |||
| Processing | Injection | |||
| Compliance | ACSDVGW W270KTWRoHS | |||
| Reinforced | 60% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Water Absorption | *** % | ISO 62 | immersion at 23°C, 2mm thk |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C – 50%RH, 2mm thk |
Biobased content | *** % | - | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Cond. 1mm/min |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Dry, 1mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | Cond. 5mm/min |
Break | *** Mpa | ISO 527-2/1A | Dry, 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | Cond. 5mm/min |
Break | *** % | ISO 527-2/1A | Dry, 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Cond. 2mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Cond. 2mm/min |
- | *** Mpa | ISO 178 | Dry, 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | 50°C/h, 50N |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.