PA610 extrusion grade with high flexibility. Toughened and heat stabilized. Good resistance to Zinc Chloride solution. Black colour.
Suitable for extrusion of pipes, profiles and cable jackets.
This grade is partially renewably-sourced (60% of base polymer by weight).
ISO 1043 : PA610-HI-T
| Original Document | Technical Datasheet(English) | |||
| Features | Good ToughnessHeat StabilizedBio-basedRenewable Resource | |||
| Additive | FlexibilizerHeat Stabilizer | |||
| Appearance | Black | |||
| Processing | ExtrusionProfile ExtrusionTube Extrusion | |||
| Compliance | RoHS | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Water Absorption | *** % | ISO 62 | immersion at 23°C, 2mm thk |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C – 50%RH, 2mm thk |
Biobased content | *** % | - | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Dry, 1mm/min |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2/1A | Dry, 50mm/min |
Tensile Elongation | |||
Nominal Tensile Strain at Break | *** % | ISO 527-2/1A | Dry, 50mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Dry, 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.