PA610 15% carbon fiber reinforced injection moulding grade. Heat stabilized. Black colour.
Suitable for parts and components requiring high mechanical properties.
The presence of carbon fibers also provides higher electrical and thermal conductivity.
This grade is partially renewably-sourced (60% of base polymer by weight).
ISO 1043 : PA610 CF15
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定导热导电生物基含可再生资源填充增强 | |||
| 添加助剂 | 热稳定剂 | |||
| 颜色形状 | 黑色 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | RoHS(欧盟电子电气设备中有害物质) | |||
| 增强填充 | 15% 碳纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.15 g/cm³ | ISO 1183 | |
吸水率 | 2.7 % | ISO 62 | immersion at 23°C, 2mm thk |
吸湿率 | 1.2 % | ISO 62 | 23°C – 50%RH, 2mm thk |
生物基含量 | 60 % | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 180 Mpa | ISO 527-2/1A | Dry, 5mm/min |
拉伸延伸率 | |||
断裂(brk) | 4 % | ISO 527-2/1A | Dry, 5mm/min |
弯曲强度 | |||
- | 245 Mpa | ISO 178 | Dry, 2mm/min |
弯曲模量 | 9500 Mpa | ISO 178 | Dry, 2mm/min |
拉伸模量 | 11600 Mpa | ISO 527-2/1A | Dry, 1mm/min |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 65 kJ/m² | ISO 179/1eU | Dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
熔融温度(Tm) | 217 °C | ISO 11357-1/-3 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.8 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1E+2 Ohm-m | IEC 60093 | Cond., 500V |
体积电阻率 | 1E+3 Ohm-m | IEC 60093 | Dry, 500V |
表面电阻率 | 1E+4 Ohm | IEC 60093 | Cond., 500V |
表面电阻率 | 1E+5 Ohm | IEC 60093 | Dry, 500V |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。