PA66 15% glass fiber reinforced injection molding grade with enhanced thermal resistance in contact with hot air. High improvement of mechanical properties retention versus standard polyamide 66 after heat ageing. Black colour.
Alternative to PPA and PA4.6 grades in medium-stiffness automotive under the bonnet applications. Continuous use temperature until 210 °C in air.
ISO 1043 : PA66-T GF15
| Original Document | Technical Datasheet(English) | |||
| Features | Heat ResistanceGood Heat AgingFilled & Reinforced | |||
| Appearance | Black | |||
| Processing | Injection | |||
| Compliance | RoHS | |||
| Reinforced | 15% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 300°C Melt Temp, 90°C Mold Temp, 60 MPa Cavity Press |
Across Flow | *** % | ISO 294-4 | 300°C Melt Temp, 90°C Mold Temp, 60 MPa Cavity Press |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Cond. 1mm/min |
Tensile Modulus | *** Mpa | ISO 527-2/1A | Dry, 1mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | Cond. 5mm/min |
Break | *** Mpa | ISO 527-2/1A | Dry, 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | Cond. 5mm/min |
Break | *** % | ISO 527-2/1A | Dry, 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Cond. 2mm/min |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Cond. 2mm/min |
- | *** Mpa | ISO 178 | Dry, 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | Dry |
Charpy Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | Cond., 500V |
Volume Resistivity | *** Ohm-m | IEC 60093 | Dry, 500V |
Surface Resistivity | *** Ohm | IEC 60093 | Cond., 500V |
Surface Resistivity | *** Ohm | IEC 60093 | Dry, 500V |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.