PBT flame retardant injection moulding grade. 30% glass fiber reinforced. Natural colour. Suitable for parts requiring fire retardancy along with high stiffness and good mechanical resistance. Rated V-0 according to UL-94.
ISO 1043 : PBT GF30 FR(16+62)
| Original Document | Technical Datasheet(English) | |||
| Features | High Stiffness/RigidityFlame RetardantHalogenatedFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Appearance | Natural Color | |||
| Processing | Injection | |||
| Compliance | RoHS | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 270°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
Across Flow | *** % | ISO 294-4 | 270°C Melt Temp, 80°C Mold Temp, 60 MPa Cavity Press |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2/1A | 1mm/min |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2/1A | 5mm/min |
Tensile Elongation | |||
Break | *** % | ISO 527-2/1A | 5mm/min |
Flexural Modulus | *** Mpa | ISO 178 | 2mm/min |
Flexural Strength | |||
- | *** Mpa | ISO 178 | 2mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/Bf | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/Af | |
Vicat Softening Temperature(VST) | *** °C | ISO 306/B50 | 50°C/h, 50N |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | UL94 | |
Glow Wire Flammability Index(GWFI) | |||
1mm | *** °C | IEC 60695-2-12 | |
2mm | *** °C | IEC 60695-2-12 | |
FMVSS | mm/min | FMVSS 302 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.