VOLTALEF 302 resin is a fluorinated polymer which presents an exceptional behavior at very low temperatures. It is usable in continuation from -200°C to +150°C with allowable peaks at 200°C. It is non-inflammability, has excellent chemical and radiation resistance, good barrier properties, is insensitivity to oxygen and water with good electrical properties.
The processing is critical but can be done by extrusion, injection and compression molding.
| 原厂资料 | 物性表-ISO(英文) | |||
| 产品特性 | 耐低温冲击阻燃电子束灭菌耐伽马射线抗紫外线抗氧化耐化学性耐水解高阻隔性 | |||
| 添加助剂 | 光稳定剂紫外线稳定剂热稳定剂 | |||
| 颜色形状 | 粉末状 | |||
| 成型方式 | 树脂转移模塑(RTM)注塑挤出薄膜挤出模压 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 2.13 g/cm³ | ISO 1183 | |
吸水率 | 0.01 % | ISO 62 | |
吸湿率 | 0.01 % | ISO 62 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 43 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 7 % | ISO 527-1/-2 | |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | |
拉伸模量 | 1400 Mpa | ISO 527-1/-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 80 kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 126 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 70 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 214 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | 55 °C | ISO 11357-1/-2 | 10°C/min |
模具温度 | 260 °C | - | Compression Molding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
氧指数(LOI) | 100 % | ISO 4589-1/-2 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 2.0E+12 Ohm-m | IEC 60093 | |
表面电阻率 | 1.0E+15 Ohm | IEC 60093 | |
绝缘强度 | 21 kV/mm | IEC 60243-1 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。