Plexiglas® V040 is a thermoplastic acrylic resin formulated for injection molding applications. It is characterized by its high heat resistance and excellent melt flow. It is available in the Asia Pacific region, where it is typically used for instrument cluster lenses, light guides, thick optics, and exterior rear combination lenses.
| 原厂资料 | 物性表-ISO(英文) 宣传册 (英文) | |||
| 产品特性 | 耐热导光耐刮擦抗紫外线耐候性高流动 | |||
| 颜色形状 | 粒状透明 | |||
| 成型方式 | 注塑 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.19 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230℃/3.8 kg | 3.3 cm³/10 min | ISO 1133 | |
熔体质量流动速率(MFR) | |||
230°C/3.8 kg | 3.6 g/10 min | ISO 1133 | |
收缩率 | |||
- | 0.2~0.6 % | ISO 294 | |
吸水率 | 0.3 % | ISO 62 | Method 1, 23°C |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 65 Mpa | ISO 527-2/1A/5 | |
断裂(brk) | 65 Mpa | ISO 527-2/1A/5 | |
拉伸延伸率 | |||
屈服(yld) | 4 % | ISO 527-2/1A/5 | |
断裂(brk) | 4 % | ISO 527-2/1A/5 | |
弯曲强度 | |||
- | 95 Mpa | ISO 178/A | Conventional Deflection |
弯曲模量 | 3000 Mpa | ISO 178/A | |
拉伸模量 | 3300 Mpa | ISO 527-2/1A/1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
- | 2 kJ/m² | ISO 179-1/1eA | |
简支梁无缺口(Charpy Unnotched) | |||
- | 20 kJ/m² | ISO 179-1/1eU | |
悬臂梁缺口(Izod Notched) | |||
- | 2 kJ/m² | ISO 180/A | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度 M | 93 M | ISO 2039-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 101 °C | ISO 75-2/B | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 97 °C | ISO 75-2/A | |
维卡软化温度(Vicat) | 105 °C | ISO 306/B50 | 50N |
维卡软化温度(Vicat) | 111 °C | ISO 306/A50 | 10N |
| 光学性能 | 值/单位 | 测试标准 | 测试条件 |
透光率 | 92 % | ASTM D1003 | 3.2 mm |
雾度 | 1 % | ASTM D1003 | 3.2 mm |
折射率 | 1.49 - | ISO 489 | Nd @ 23°C |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。