Polyether block amide Pebax® 7033 SP 01 resin is a thermoplastic elastomer made of flexible polyether and rigid polyamide.
This SP grade has been developed to be heat and UV resistant.
Main applications:
Athletic foot wear components.
Ski shoes.
Tennis rocket bumpers.
Zip fasteners.
Packaging:
This grade is delivered dried in sealed packaging (20 to 25 kg bags) ready to be processed.
Shelf Life:
Two years from the deliverty. For any use above this limit, please refer to our technical services.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热热稳定电镀/真空镀抗紫外线 | |||
| 添加助剂 | 光稳定剂紫外线稳定剂热稳定剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 树脂转移模塑(RTM)浇铸注塑挤出型材挤出薄膜挤出热成型 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.01 g/cm³ | ISO 1183 | Cond. |
密度 | 1.01 g/cm³ | ISO 1183 | Dry |
收缩率 | |||
纵向(Flow) | 1.2 % | ISO 294-4, 2577 | Dry |
横向(Across Flow) | 1.5 % | ISO 294-4, 2577 | Dry |
吸水率 | 1.1 % | ISO 62 | Dry |
吸湿率 | 0.7 % | ISO 62 | Dry |
熔体密度 | 0.83 g/cm³ | - | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 22 Mpa | ISO 527-1/-2 | Cond. |
屈服(yld) | 23 Mpa | ISO 527-1/-2 | Dry |
断裂(brk) | 54 Mpa | ISO 527-1/-2 | Dry, TPE |
10%延伸率时 | 22 Mpa | ISO 527-1/-2 | Dry, TPE |
100%延伸率时 | 21 Mpa | ISO 527-1/-2 | Dry, TPE |
拉伸延伸率 | |||
屈服(yld) | 20 % | ISO 527-1/-2 | Cond. |
屈服(yld) | 22 % | ISO 527-1/-2 | Dry |
断裂(brk) | 300 % | ISO 527-1/-2 | Dry, TPE |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Cond. |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | Dry |
拉伸模量 | 390 Mpa | ISO 527-1/-2 | Cond. |
拉伸模量 | 414 Mpa | ISO 527-1/-2 | Dry |
撕裂强度 | 149 kN/m | ISO 34 | Dry, TPE |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 20 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | 120 kJ/m² | ISO 179/1eA | Cond. |
23℃ (73℉) | NB kJ/m² | ISO 179/1eA | Dry |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Cond. |
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | Dry |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Cond. |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | Dry |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 61 D | ISO 7619-1 | Dry, 15s |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 99 °C | ISO 75-1/-2 | Dry |
维卡软化温度(Vicat) | 164 °C | ISO 306 | Dry, 50°C/h 50N |
比热容 | 2700 J/kg-K | - | |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 160 E-6/K | ISO 11359-1/-2 | Dry |
熔融温度(Tm) | 172 °C | ISO 11357-1/-3 | Dry, 10°C/min |
导热系数 | 0.2 W/(m K) | - | |
加工温度 | 260 °C | - | Injection molding |
模具温度 | 60 °C | - | Injection molding |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | IEC 60695-11-10 | Dry |
HB | 3.1 mm | IEC 60695-11-10 | Dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
表面电阻率 | 4.0E+13 Ohm | IEC 60093 | Cond. |
相对漏电起痕指数(CTI ) | |||
- | 600 - | IEC 60112 | Cond. |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。