LOTADER® HX8290 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.
Applications
Due to its properties, reactivity, fluidity and compatibility with tackifying resins and waxes, LOTADER ® HX8290 is suitable as additive for hot melt adhesive formulations and as coupling agent in mineral filled compounds such as halogen free flame retardant wires and cables.
| Original Document | Technical Datasheet(English) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ISO 1133 | |
Ethyl Acrylate Content | *** % | Company | |
Maleic Anhydride Content | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ISO 527 | |
Tensile Elongation | |||
Break | *** % | ISO 527 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10N |
Melt Temperature(Tm) | *** °C | ISO 11357-3 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.