LOTADER® 4700 is a random terpolymer of ethylene, acrylic ester and maleic anhydride, polymerized by high-pressure autoclave process.
Acrylic ester brings softness and polarity, while keeping high thermal stability during processing.
The high content of acrylic ester leads to high flexibility (low-cristallinity) and high impact absorption behaviour.
Maleic anhydride gives reactivity (versus OH and NH 2 groups), leading to optimal dispersion during melt mixing with engineering thermoplastics (mainly polyamides).
Applications
Due to its properties (softness, reactivity), LOTADER® 4700 is suitable as modifier to improve the impact strength of polyamides (PA6, PA66, PA12 etc.). It can also be used as a compatibilizer for polyamides / polyolefins blends.
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactHeat StabilizedSoft | |||
| Appearance | Pellets/Granules | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
190℃/2.16 kg | *** g/10min | ISO 1133 | |
Ethyl Acrylate Content | *** % | Company | |
Maleic Anhydride Content | *** % | Internal | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | |
Flexural Modulus | *** Mpa | ISO 178 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | 10N |
Melt Temperature(Tm) | *** °C | ISO 11357-3 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.