Kynar Flex® resins are fluorinated thermoplastic copolymers.
Kynar Flex® 3120-50 is a pelletized flexible, semi-crystalline VF2 based copolymer. It can be molded or extruded and has a useful temperature range from -40°C - 150°C. Kynar Flex® 3120-50 has a UL RTI of 150°C.
Kynar Flex® 3120-50 can be used in compounding for cross-linkable wire and cable as well as both wire applications requiring low temperature flexibility and high temperature resistance.
Kynar Flex® 3120-50 also finds use as a polymer processing aid (PPA) for polyolefins. The use of Kynar Flex® 3120-50 or Kynar Flex 3121-50 at 200 -1000 ppm levels reduces extruder pressure, improves surface finish, reduces die build up, and improves gauge control.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击耐热热稳定抗紫外线 | |||
| 添加助剂 | 紫外线稳定剂热稳定剂 | |||
| 颜色形状 | 粒状 | |||
| 成型方式 | 注塑挤出型材挤出 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.78 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230°C/5.0 kg | 0.5 cm³/10 min | ISO 1133 | |
吸水率 | 0.03 % | ISO 62 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 27 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 15 % | ISO 527-1/-2 | |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | |
拉伸模量 | 700 Mpa | ISO 527-1/-2 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | NB kJ/m² | ISO 179/1eA | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 50 °C | ISO 75-1/-2 | |
熔融温度(Tm) | 165 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | -36 °C | ISO 11357-1/-2 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1 mm | IEC 60695-11-10 | |
V-0 | 1.5 mm | IEC 60695-11-10 | |
5VA | 1 mm | IEC 60695-11-10 | |
氧指数(LOI) | 43 % | ISO 4589 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。