Kynar Flex® resins are fluorinated thermoplastic copolymers.
Outstanding characteristics: chemical resistance, imperviousness to UV, high barrier properties, high purity, good mechanical and thermo-mechanical properties.
Main applications: corrosion protection in the chemical industry, coating (painting, co-extrusion), off shore, wire and cable.
Kynar Flex® 2801 resin is the powder form of the Kynar Flex® 2800-00 resin. To be used an additive in LLDPE to improve the extrusion rate.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 热稳定易涂装抗紫外线耐候性耐化学性高阻隔性 | |||
| 添加助剂 | 紫外线稳定剂热稳定剂 | |||
| 颜色形状 | 粉末状 | |||
| 成型方式 | 共挤涂装 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.78 g/cm³ | ISO 1183 | |
熔体体积流动速率(MVR) | |||
230°C/5.0 kg | 0.5 cm³/10 min | ISO 1133 | |
吸水率 | 0.03 % | ISO 62 | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
屈服(yld) | 27 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
屈服(yld) | 15 % | ISO 527-1/-2 | |
标称断裂伸长率 | 50 % | ISO 527-1/-2 | |
拉伸模量 | 700 Mpa | ISO 527-1/-2 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 48 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 79 °C | ISO 306 | 50 °C/h 50N |
线性膨胀系数(CLTE) | |||
- | 160 E-6/K | ISO 11359-1/-2 | |
熔融温度(Tm) | 143 °C | ISO 11357-1/-3 | 10°C/min |
玻璃化温度(Tg) | -36 °C | ISO 11357-1/-2 | 10°C/min |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
V-0 | 1.5 mm | IEC 60695-11-10 | |
氧指数(LOI) | 43 % | ISO 4589 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 2.0E+12 Ohm-m | IEC 60093 | |
介电常数(DK) | |||
1MHz | 7 - | IEC 60250 | |
耗散因数(DF) | |||
1MHz | 2330 E-4 | IEC 60250 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。