| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高刚性食品接触级耐燃油耐油 | |||
| 成型方式 | 注塑 | |||
| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
|---|---|---|---|
密度/比重 | *** g/cm³ | ASTM D792 | |
收缩率 | |||
纵向(Flow) | *** % | ASTM D955 | 2.54 mm |
横向(Across Flow) | *** % | ASTM D955 | 2.54 mm |
磨耗 | *** mg/1000cy | ASTM D 3489 | H-18, 1,000-g Load |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸强度 | |||
- | *** Mpa | ASTM D 412 | |
50%延伸率时 | *** Mpa | ASTM D 412 | |
100%延伸率时 | *** Mpa | ASTM D 412 | |
300%延伸率时 | *** Mpa | ASTM D 412 | |
拉伸延伸率 | |||
断裂(brk) | *** % | ASTM D 412 | |
弯曲模量 | *** Mpa | ASTM D790 | -22°F (-30°C) |
弯曲模量 | *** Mpa | ASTM D790 | 158°F (70°C) |
弯曲模量 | *** Mpa | ASTM D790 | 73°F (23°C) |
撕裂强度 | *** kN/m | ASTM D 624 | Die C |
压缩永久形变 | *** % | ASTM D 395 | 22 Hours at 158°F (70°C) |
压缩永久形变 | *** % | ASTM D 395 | 22 Hours at 73°F (23°C) |
压缩永久形变 | *** % | ASTM D 395 | Postcured, 22 Hours at 158°F (70°C) |
压缩永久形变 | *** % | ASTM D 395 | Postcured, 22 Hours at 73°F (23°C) |
抗压强度 | *** Mpa | ASTM D 575 | 10% Deflection |
抗压强度 | *** Mpa | ASTM D 575 | 15% Deflection |
抗压强度 | *** Mpa | ASTM D 575 | 2% Deflection |
抗压强度 | *** Mpa | ASTM D 575 | 20% Deflection |
抗压强度 | *** Mpa | ASTM D 575 | 25% Deflection |
抗压强度 | *** Mpa | ASTM D 575 | 5% Deflection |
抗压强度 | *** Mpa | ASTM D 575 | 50% Deflection |
回弹性 | *** % | ASTM D 2632 | Bayshore Resilience |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
脆化温度 | *** °C | ASTM D 746 | |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
邵氏硬度 D | *** D | ASTM D 2240 | |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | |
维卡软化温度(Vicat) | *** °C | ASTM D1525 | Rate A |
线性膨胀系数(CLTE) | |||
- | *** E-6 mm/mm/℃ | ASTM D 696 | |
玻璃化温度(Tg) | °C | Internal |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。