Extrusion- and injection molding grade; with special UV stabilizers; very good hydrolysis and microbial resistance; good low-temperature flexibility; free from plasticizers; high moisture vapor transmission rate; Application; breathable films; Films; Sports shoe soles; hard - soft systems
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | High Impact at Low TemperaturPhthalates/Plasticizer free (PAEs)UV StabiltiyHydrolysis Resistance | |||
| Additive | UV-Stabilizer | |||
| Processing | InjectionExtrusion | |||
| Diagrams | Dynamic Shear modulus-temperatureStress-strain (TPE) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | 23 °C |
Abrasion resistance | *** mm³ | ISO 4649 | Method A |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | DIN 53504 | 200 mm/min |
at 100% strain | *** Mpa | DIN 53504 | 200 mm/min |
at 300% strain | *** Mpa | DIN 53504 | 200 mm/min |
Tensile Elongation | |||
Break | *** % | DIN 53504 | 200 mm/min |
Tear Strength | *** kN/m | ISO 34 | 500 mm/min |
Compression Set | *** % | ISO 815 | 24 h; 70 °C, Method A |
Compression Set | *** % | ISO 815 | 24 h; 70 °C, Method C |
Compression Set | *** % | ISO 815 | 72 h; 23 °C |
Rebound Resilience | *** % | ISO 4662 | 23 °C/50 % r. h. |
Tensile Storage Modulus | *** Mpa | ISO 6721-1,-4 | -20 °C |
Tensile Storage Modulus | *** Mpa | ISO 6721-1,-4 | 20 °C |
Tensile Storage Modulus | *** Mpa | ISO 6721-1,-4 | 60 °C |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ISO 7619-1 | 1s |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.