injection molding grade; no yellowing under the action of UV light; improved microbial resistance; good low-temperature flexibility; Improved hydrolysis resistance; Application; automotive interior applications
| Original Document | Technical Datasheet(English) Technical Datasheet(Chinese) | |||
| Features | High Impact at Low TemperaturUV StabiltiyHydrolysis Resistance | |||
| Processing | Injection | |||
| Diagrams | Stress-strain (TPE) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | 23 °C |
Abrasion resistance | *** mm³ | ISO 4649 | Method A |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Break | *** Mpa | DIN 53504 | 200 mm/min |
at 10% strain | *** Mpa | DIN 53504 | 200 mm/min |
at 50% strain | *** Mpa | ISO 527 | 200 mm/min |
at 100% strain | *** Mpa | DIN 53504 | 200 mm/min |
at 300% strain | *** Mpa | DIN 53504 | 200 mm/min |
Tensile Elongation | |||
Break | *** % | DIN 53504 | 200 mm/min |
Tear Strength | *** kN/m | ISO 34 | 500 mm/min |
Compression Set | *** % | ISO 815 | 24 h; 70 °C, Method A |
Compression Set | *** % | ISO 815 | 24 h; 70 °C, Method C |
Compression Set | *** % | ISO 815 | 72 h; 23 °C |
Rebound Resilience | *** % | ISO 4662 | 23 °C/50 % r. h. |
Tensile Storage Modulus | *** Mpa | ISO 6721-1,-4 | -20 °C |
Tensile Storage Modulus | *** Mpa | ISO 6721-1,-4 | 20 °C |
Tensile Storage Modulus | *** Mpa | ISO 6721-1,-4 | 60 °C |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ISO 7619-1 | 1s |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.