Ultrasint PP is especially developed for the SLS process as an alternative to polyamide. In contrast to commonly used polyamides, Ultrasint PP has an excellent plasticity, higher elongation, low moisture absorption and durability. The fields of application vary widely, from automotive, electrical and sport industries, health care and orthopedic products. Ultrasint PP works perfectly for hinges and clips. It allows post processing like thermoforming or sealing. Ultrasint PP is resistant to most acids and bases and has a slight translucent appearance. Due to its attractive commercial value, it is an interesting material to expand 3D printing applications and volumes. Ultrasint PP has been successfully tested on most common SLS printers. Parameters for printing will be provided.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 高耐久性耐酸耐碱 | |||
| 颜色形状 | 粉末状半透明白色 | |||
| 成型方式 | 激光烧结(SLS)3D打印 | |||
| 物理性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
|---|---|---|---|---|
密度 | 0.89/ * | g/cm³ | ISO 61 | Printed Part |
粒子大小 | 67~77/ * | micrometer | Internal | d50 |
堆积(视)密度 | 0.33/ * | g/cm³ | ISO 1068 | |
| 机械性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
拉伸强度 | ||||
- | 25/ * | Mpa | ISO 527-2 | x-direction |
拉伸延伸率 | ||||
断裂(brk) | 50/ * | % | ISO 527-2 | x-direction |
弯曲模量 | 1150/ * | Mpa | ISO 178 | x-direction |
拉伸模量 | 1400/ * | Mpa | ISO 527-2 | x-direction |
| 冲击性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
简支梁无缺口(Charpy Unnotched) | ||||
- | 22/ * | kJ/m² | ISO 179 | x-direction |
| 热学性能 | 干态/湿态 | 单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | ||||
0.45 Mpa (66 psi)（4.6kg/cm²） | 71/ * | °C | ISO 75-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 56/ * | °C | ISO 75-2 | |
熔融温度(Tm) | 139/ * | °C | ISO 11357-3 | 20 K/min |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。