Petra 130 is a 30% glass fiber reinforced polyethylene terephthalate injection molding compound. It is available in natural and pigmented versions. It exhibits a superb combination of performance properties including high strength and stiffness at elevated temperatures with good chemical resistance and dimensional stability.
Applications
Petra 130 is generally recommended for applications such as automotive door lock components, housings, gears and electrical and mechanical components.
| 原厂资料 | 物性表-ISO(英文) 物性表-ASTM(英文) | |||
| 产品特性 | 高强度高刚性耐热尺寸稳定耐化学性填充增强 | |||
| 颜色形状 | 粒状本色 | |||
| 成型方式 | 注塑 | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.55 g/cm³ | ISO 1183 | |
比重 | 1.55 - | ASTM D792 | |
收缩率 | |||
- | 0.4 % | Internal | |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 210 Mpa | ISO 527 | -40℃ |
断裂(brk) | 65 Mpa | ISO 527 | 120℃ |
断裂(brk) | 50 Mpa | ISO 527 | 150℃ |
断裂(brk) | 155 Mpa | ISO 527 | 23℃ |
断裂(brk) | 80 Mpa | ISO 527 | 80℃ |
断裂(brk) | 210 Mpa | ASTM D638 | -40°C (-40°F) |
断裂(brk) | 65 Mpa | ASTM D638 | 121°C (250°F) |
断裂(brk) | 155 Mpa | ASTM D638 | 23°C (73°F) |
断裂(brk) | 80 Mpa | ASTM D638 | 80°C (176°F) |
拉伸延伸率 | |||
断裂(brk) | 3 % | ASTM D638 | 23°C (73°F) |
断裂(brk) | 3.5 % | ISO 527 | 23℃ |
弯曲强度 | |||
- | 275 Mpa | ASTM D790 | -40°C (-40°F) |
- | 85 Mpa | ASTM D790 | 121°C (250°F) |
- | 240 Mpa | ASTM D790 | 23°C (73°F) |
- | 170 Mpa | ASTM D790 | 65°C (149°F) |
- | 105 Mpa | ASTM D790 | 90°C (194°F) |
弯曲模量 | 9660 Mpa | ASTM D790 | -40°C (-40°F) |
弯曲模量 | 2830 Mpa | ASTM D790 | 121°C (250°F) |
弯曲模量 | 8970 Mpa | ASTM D790 | 23°C (73°F) |
弯曲模量 | 6130 Mpa | ASTM D790 | 65°C (149°F) |
弯曲模量 | 3440 Mpa | ASTM D790 | 90°C (194°F) |
拉伸模量 | 10400 Mpa | ISO 527 | -40℃ |
拉伸模量 | 2940 Mpa | ISO 527 | 120℃ |
拉伸模量 | 2360 Mpa | ISO 527 | 150℃ |
拉伸模量 | 10200 Mpa | ISO 527 | 23℃ |
拉伸模量 | 4950 Mpa | ISO 527 | 80℃ |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 9 kJ/m² | ISO 179 | |
悬臂梁缺口(Izod Notched) | |||
23℃ (73℉) | 95 J/m | ASTM D256 | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
洛氏硬度R | 118 R | ASTM D785 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 240 °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 220 °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 210 °C | ISO 75 | |
相对温度指数(RTI) | |||
冲击Imp,0.75/0.8mm | 140 °C | UL 746B | |
冲击Imp,1.5/1.6 mm | 140 °C | UL 746B | |
冲击Imp,3.0/3.2 mm | 140 °C | UL 746B | |
电气Elec,0.75/0.8mm | 140 °C | UL 746B | |
电气Elec,1.5/1.6 mm | 140 °C | UL 746B | |
电气Elec,3.0/3.2 mm | 140 °C | UL 746B | |
强度Str,0.75/0.8mm | 140 °C | UL 746B | |
强度Str,1.5/1.6 mm | 140 °C | UL 746B | |
强度Str,3.0/3.2 mm | 140 °C | UL 746B | |
线性膨胀系数(CLTE) | |||
- | 23 E-6 mm/mm/℃ | ASTM D E831 | |
熔融温度(Tm) | 245 °C | ASTM D3418 | |
熔融温度(Tm) | 245 °C | ISO 3146 | |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.75 mm | UL94 | |
HB | 1.5 mm | UL94 | |
HB | 3 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-cm | ASTM D257 | 1.5 mm |
体积电阻率 | 1.0E+13 Ohm-cm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 3.7 - | IEC 60250 | |
1MHz | 3.5 - | IEC 60250 | |
耗散因数(DF) | |||
100Hz | 200 E-4 | IEC 60250 | |
1MHz | 200 E-4 | IEC 60250 | |
绝缘强度 | 22 kV/mm | ASTM D149 | Short Time, 1.5 mm |
绝缘强度 | 40 kV/mm | IEC 60243-1 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。