Low density I-skin urethane (PU) foam system (natural color)
HFC 245fa-blown, two-component microcellular polyurethane foam system designed for molding of miscellaneous Integral Skin articles that require good skin at relatively low molded densities. Depending on the application requirements and the processing conditions this system can provide
Exceptional skin formation when casted in metal tools at low mold temperatures
Wide range of molded densities from 10 to 25 pcf
Hardness range from 10 to 70 Shore A
Wide processing window on both low-pressure and high-pressure equipment
| Original Document | Technical Datasheet(English) | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1622 | Hand-Mix at 77° F |
Density/Specific Gravity | *** g/cm³ | ASTM D 1622 | High Pressure at 85° F |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
- | *** Mpa | ASTM D 412 | skin one side, Hand-Mix at 77° F |
- | *** Mpa | ASTM D 412 | skin one side, High Pressure at 85° F |
Tensile Elongation | |||
- | *** % | ASTM D 412 | skin one side, Hand-Mix at 77° F |
- | *** % | ASTM D 412 | skin one side, High Pressure at 85° F |
Tear Strength | *** N/mm | ASTM D 624 | Die-C, Hand-Mix at 77° F |
Tear Strength | *** N/mm | ASTM D 624 | Die-C, High Pressure at 85° F |
Tear Strength | *** N/mm | ASTM D 624 | Split, Hand-Mix at 77° F |
Tear Strength | *** N/mm | ASTM D 624 | Split, High Pressure at 85° F |
Compression Set | *** % | ASTM D 395 | Ct 22 hrs at 70°C, Hand-Mix |
Compression Set | *** % | ASTM D 395 | Ct 22 hrs at 70°C, High Pressure |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Shore A hardness | *** A | ASTM D 2240 | Hand-Mix at 77° F |
Shore A hardness | *** A | ASTM D 2240 | High Pressure at 85° F |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.