Eastman Tritan™ MP100 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Film and sheet manufactured from this new-generation copolyester can be thermoformed with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan™ MP100 copolyester is suitable for use with most forms of sterilization including radiation and ethylene oxide. It is NOT suitable for autoclave/steam sterilization. Eastman Tritan™ MP100 copolyester has been formulated for use in medical film, sheet, and packaging applications.
| Original Document | Technical Datasheet(English) | |||
| Features | Good ToughnessHeat ResistanceBPA FreePhthalates/Plasticizer free (PAEs)E-beam SterilizableGamma ResistanceEtO sterilizableChemical Resistance | |||
| Appearance | Pellets/GranulesOpaque Color | |||
| Processing | ExtrusionSheet ExtrusionFilm ExtrusionThermoforming | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D 1505 | 250 µm film |
Water Absorption | *** % | ASTM D570 | 24 hours |
Abrasion resistance | *** % | ASTM D 1044 | at 25 cycles |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Instrumented Impact Energy | |||
23℃ (73℉)Total Energy | *** J | ASTM D3763 | 250 µm film |
Brittleness Temperature | *** °C | ASTM D 1790 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Specific Heat | *** J/kg-K | DSC | 100°C |
Specific Heat | *** J/kg-K | DSC | 150°C |
Specific Heat | *** J/kg-K | DSC | 200°C |
Specific Heat | *** J/kg-K | DSC | 250°C |
Specific Heat | *** J/kg-K | DSC | 60°C |
Coefficient of Linear Thermal Expansion | |||
- | *** E-6 mm/mm/℃ | ASTM D 696 | |
Glass Transition Temperature | *** °C | DSC | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | ASTM D1003 | Total |
Light Transmission | *** % | Internal | 380 nm UV |
Haze | *** % | ASTM D1003 | |
Refractive Index | *** - | ASTM D542 | |
Gloss | *** - | ASTM D 2457 | 60° |
| Film | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D 882 | 250 µm film, M.D. |
Yield | *** Mpa | ASTM D 882 | 250 µm film, T.D. |
Break | *** Mpa | ASTM D 882 | 250 µm film, M.D. |
Break | *** Mpa | ASTM D 882 | 250 µm film, T.D. |
Tensile Elongation | |||
Yield | *** % | ASTM D 882 | 250 µm film, M.D. |
Yield | *** % | ASTM D 882 | 250 µm film, T.D. |
Break | *** % | ASTM D 882 | 250 µm film, M.D. |
Break | *** % | ASTM D 882 | 250 µm film, T.D. |
Tensile Modulus | *** Mpa | ASTM D 882 | 250 µm film, M.D. |
Tensile Modulus | *** Mpa | ASTM D 882 | 250 µm film, T.D. |
Elmondorf Tear | *** N | ASTM D 1922 | 250 µm film, M.D. |
Elmondorf Tear | *** N | ASTM D 1922 | 250 µm film, T.D. |
Trouser Tear | *** kN/m | ISO 6383-1 | 250 µm film, M.D. |
Trouser Tear | *** kN/m | ISO 6383-1 | 250 µm film, T.D. |
Dart Drop Impact | *** g | ASTM D 1709 | 250 µm film, -18°C |
Dart Drop Impact | *** g | ASTM D 1709 | 250 µm film, -30°C |
Dart Drop Impact | *** g | ASTM D 1709 | 250 µm film, 23°C |
Water Vapor Transmission Rate | *** g/m²/24 hr | ASTM F 1249 | 23°C, 250 µm film |
Water Vapor Transmission Rate | *** g/m²/24 hr | ASTM F 1249 | 38°C, 250 µm film |
Oxygen permeability | *** cm³·mm/m²/atm/24 hr | ASTM D 3985 | 250 µm film |
Carbon Dioxide transm. rate | *** cm³·mm/m²/atm/24 hr | ASTM D 1434 | 250 µm film |
Surface Energy | *** dynes/cm | ASTM D 5946 | Polar |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.