Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic plastics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resistance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer content increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected ambers, or smoke transparents and black translucent. Color concentrates are available in let-down ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 530-10 contains an odor mask and has a plasticizer level of 10%.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthGood ToughnessHigh GlossSoft | |||
| Additive | Plasticizer | |||
| Appearance | Pellets/GranulesNatural ColorClear/TransparentTranslucentBlackBrown | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Mold Shrinkage | |||
- | ***~*** % | ASTM D955 | |
Water Absorption | *** % | ASTM D570 | 24 h immersion |
Plasticizer | *** % | - | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | |
Break | *** Mpa | ASTM D638 | |
Tensile Elongation | |||
Break | *** % | ASTM D638 | |
Flexural Modulus | *** Mpa | ASTM D790 | |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** J/m | ASTM D256 | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell R | *** R | ASTM D785 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | Conditioned 4 hours @ 70°C |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | Conditioned 4 hours @ 70°C |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Conditioned 4 hours @ 70°C |
Specific Heat | ***~*** J/kg-K | DSC | 23°C |
Coefficient of Linear Thermal Expansion | |||
- | ***~*** E-6 mm/mm/℃ | ASTM D 696 | |
Thermal Conductivity | ***~*** W/(m K) | ASTM C 177 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | ***~*** Ohm-cm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
1MHz | ***~*** - | ASTM D 150 | |
Dissipation Factor | |||
1MHz | ***~*** E-4 | ASTM D150 | |
Dielectric Strength | ***~*** kV/mm | ASTM D149 | |
| Optical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Light Transmission | *** % | Internal | 1.52 mm |
Haze | *** % | ASTM D1003 | 1.52 mm |
Refractive Index | ***~*** - | ASTM D542 | nD |
| Additional Information | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Soluble Matter Loss | *** % | ASTM D 570 | |
Weight Loss on Heating | *** % | ASTM D 706 | 72 hours @ 80°C |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.