| 物理性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
密度/比重 |
*** g/cm³
| ASTM D792 | |
密度/比重 |
*** g/cm³
| ASTM D 1505 | Crystalline |
粘度 |
*** -
| Internal | 264 µm film |
熔体密度 |
*** g/cm³
| - | 285°C |
堆积(视)密度 |
*** g/cm³
| ASTM D 1895 | Poured |
堆积(视)密度 |
*** g/cm³
| ASTM D 1895 | Vibrated |
| 机械性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸模量 |
*** Mpa
| ASTM D638 | |
拉伸模量 |
*** Mpa
| ISO 527 | |
拉伸强度 | | | |
屈服(yld) |
*** Mpa | ASTM D638 | |
屈服(yld) |
*** Mpa | ISO 527 | |
断裂(brk) |
*** Mpa | ISO 527 | |
断裂(brk) |
*** Mpa | ASTM D638 | |
弯曲模量 |
*** Mpa
| ASTM D790 | |
弯曲模量 |
*** Mpa
| ISO 178 | |
弯曲强度 | | | |
屈服(yld) |
*** Mpa | ASTM D790 | |
屈服(yld) |
*** Mpa | ISO 178 | |
| 冲击性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
悬臂梁缺口(Izod Notched) | | | |
-40℃ (-40℉) |
*** J/m | ASTM D256 | |
-40℃ (-40℉) |
*** kJ/m² | ISO 180 | |
23℃ (73℉) |
*** J/m | ASTM D256 | |
23℃ (73℉) |
*** kJ/m² | ISO 180 | |
悬臂梁无缺口(Izod Unnotched) | | | |
-40℃ (-40℉) |
*** J/m | ASTM D 4812 | |
-40℃ (-40℉) |
*** kJ/m² | ISO 180 | |
-30℃ (-22℉) |
*** J/m | ASTM D 4812 | |
-30℃ (-22℉) |
*** kJ/m² | ISO 180 | |
-20℃ (-4℉) |
*** J/m | ASTM D 4812 | |
-20℃ (-4℉) |
*** kJ/m² | ISO 180 | |
23℃ (73℉) |
*** J/m | ASTM D4812 | |
23℃ (73℉) |
*** kJ/m² | ISO 180 | |
仪器化落镖冲击能量 | | | |
-40℃ (-40℉)峰值 |
*** J | ASTM D3763 | 2.5 mm |
-40℃ (-40℉)峰值 |
*** J | ASTM D3763 | 3.2 mm |
-40℃ (-40℉)峰值 |
*** J | ISO 6603-2 | 2.5 mm |
-40℃ (-40℉)峰值 |
*** J | ISO 6603-2 | 3.2 mm |
23℃ (73℉)峰值 |
*** J | ASTM D3763 | 2.5 mm |
23℃ (73℉)峰值 |
*** J | ASTM D3763 | 3.2 mm |
23℃ (73℉)峰值 |
*** J | ISO 6603-2 | 2.5 mm |
23℃ (73℉)峰值 |
*** J | ISO 6603-2 | 3.2 mm |
| 硬度性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
洛氏硬度R |
*** R
| ASTM D785 | |
| 热学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
热变形温度(HDT) | | | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ASTM D648 | |
0.45 Mpa (66 psi)（4.6kg/cm²） |
*** °C | ISO 75 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ASTM D648 | |
1.8 Mpa (264 psi)（18.6kg/cm²） |
*** °C | ISO 75 | |
比热容 |
*** J/kg-K
| ASTM E 1269 | 100°C |
比热容 |
*** J/kg-K
| ASTM E 1269 | 200°C |
比热容 |
*** J/kg-K
| ASTM E 1269 | 23°C |
比热容 |
*** J/kg-K
| ASTM E 1269 | 280°C |
比热容 |
*** J/kg-K
| ASTM E 1269 | 80°C |
结晶温度 |
*** °C
| ASTM D 3418 | |
熔化热 |
*** J/g
| ASTM E 793 | |
| 光学性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
透光率 |
*** %
| ASTM D1003 | Regular Transmittance, 264 µm film |
透光率 |
*** %
| ASTM D1003 | Total Transmittance, 264 µm film |
透光率 |
*** %
| ASTM D 1746 | Transparency, 264 µm film |
雾度 |
*** %
| ASTM D1003 | 264 µm film |
光泽度 |
*** -
| ASTM D 2457 | 60°, 264 µm film |
| 薄膜性能 | 值/单位(登录后可见) | 测试标准 | 测试条件 |
拉伸强度 | | | |
屈服(yld) |
*** Mpa | ASTM D 882 | 264 µm film, M.D. |
屈服(yld) |
*** Mpa | ASTM D 882 | 264 µm film, T.D. |
断裂(brk) |
*** Mpa | ASTM D 882 | 264 µm film, M.D. |
断裂(brk) |
*** Mpa | ASTM D 882 | 264 µm film, T.D. |
拉伸延伸率 | | | |
屈服(yld) |
*** % | ASTM D 882 | 264 µm film, M.D. |
屈服(yld) |
*** % | ASTM D 882 | 264 µm film, T.D. |
断裂(brk) |
*** % | ASTM D 882 | 264 µm film, M.D. |
断裂(brk) |
*** % | ASTM D 882 | 264 µm film, T.D. |
拉伸模量 |
*** Mpa
| ASTM D 882 | 264 µm film, M.D. |
拉伸模量 |
*** Mpa
| ASTM D 882 | 264 µm film, T.D. |
埃尔曼多夫撕裂 |
*** g
| ASTM D 1922 | 264 µm film, M.D. |
埃尔曼多夫撕裂 |
*** g
| ASTM D 1922 | 264 µm film, T.D. |
裤形撕裂 |
*** kN/m
| ISO 6383-1 | 264 µm film, M.D. |
裤形撕裂 |
*** kN/m
| ISO 6383-1 | 264 µm film, T.D. |
落锤冲击 |
*** g
| ASTM D 1709 | 264 µm film, -18°C |
落锤冲击 |
*** g
| ASTM D 1709 | 264 µm film, 23°C |
水蒸气渗透系数 |
*** g/m²/24 hr
| ASTM F 372 | 264 µm film |
氧渗透 |
*** cm³·mm/m²/atm/24 hr
| ASTM D 3985 | 264 µm film |
二氧化碳渗透 |
*** cm³·mm/m²/atm/24 hr
| ASTM D 1434 | 264 µm film |