Typical Applications: alpine ski boots, noiseless gears, conveyor belts
PA 12 elastomers, the most important subgroup of polyamide elastomers, belong to the increasingly important material class of thermoplastic elastomers (TPE). Because of their excellent properties, they are indispensable in many applications.
PA 12 elastomers are block copolymers consisting of PA 12 segments and polyether segments. PA 12-rich products have the major properties of PA 12, while the elastomer characteristics become more apparent with increasing polyether content. That is the polymers become more flexible, with higher impact strength at cold temperatures.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐低温冲击易着色易成型易涂装抗紫外线耐化学性耐溶剂弹性体 | |||
| 添加助剂 | 紫外线稳定剂热稳定剂 | |||
| 颜色形状 | 粒状本色黑色 | |||
| 成型方式 | 注塑挤出 | |||
| 曲线坐标点 | N粘度-剪切速度剪切应力-剪切速率应力-应变正割模量-应变应力-应变 (等时的) 23°C (湿态)蠕变模量-时间 23°C (湿态)比容-温度(pvT)拉伸模量-温度应力-应变(热塑弹性体) | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.03 g/cm³ | ISO 1183 | |
收缩率 | |||
纵向(Flow) | 0.6~1.1 % | ISO 294-4 | 3mm |
横向(Across Flow) | 0.9~1.4 % | ISO 294-4 | 3mm |
吸水率 | 1.1 % | ISO 62 | 23 °C, saturation |
粘度 | 190 cm³/g | ISO 307 | Viscosity number |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
50%延伸率时 | 23 Mpa | ISO 527-1/-2 | |
- | 42 Mpa | ISO 527-1/-2 | |
拉伸延伸率 | |||
断裂(brk) | 200 % | ISO 527-1/-2 | |
拉伸模量 | 370 Mpa | ISO 527-1/-2 | |
拉伸蠕变模量 | |||
1000h | 200 Mpa | ISO 899-1 | |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
-30℃ (-22℉) | 8 kJ/m² | ISO 179/1eA | Complete Break |
23℃ (73℉) | 120 kJ/m² | ISO 179/1eA | Partial Break |
简支梁无缺口(Charpy Unnotched) | |||
-30℃ (-22℉) | NB kJ/m² | ISO 179/1eU | |
23℃ (73℉) | NB kJ/m² | ISO 179/1eU | |
| 硬度性能 | 值/单位 | 测试标准 | 测试条件 |
邵氏硬度 D | 62 D | ISO 868 | |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | 100 °C | ISO 75-1/-2 | |
1.8 Mpa (264 psi)（18.6kg/cm²） | 45 °C | ISO 75-1/-2 | |
维卡软化温度(Vicat) | 165 °C | ISO 306 | 10 N |
维卡软化温度(Vicat) | 110 °C | ISO 306 | 50 N |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 200 E-6/K | ISO 11359 | 23-55 °C |
横向(Across Flow) | 200 E-6/K | ISO 11359 | 23-55 °C |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 1.6 mm | UL94 | |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+12 Ohm-cm | IEC 60093 | |
表面电阻率 | 1.0E+14 Ohm | IEC 60093 | |
介电常数(DK) | |||
100Hz | 9 - | IEC 60250 | 23 °C |
1MHz | 4 - | IEC 60250 | 23 °C |
耗散因数(DF) | |||
100Hz | 1000 E-4 | IEC 60250 | 23 °C |
1MHz | 1200 E-4 | IEC 60250 | 23 °C |
相对漏电起痕指数(CTI ) | |||
溶液A | 600 V | IEC 60112 | |
绝缘强度 | 39 kV/mm | IEC 60243-1 | K20/P50 |
此物性表中的信息由阿技材料库从该材料的生产商处获得。阿技材料库尽最大努力确保此数据的准确性。 但是阿技材料库对这些数据值不承担任何责任，并强烈建议在最终选择材料前，就数据值与材料供应商进行验证。