Vydyne R533H NAT is 33% glass-fiber reinforced, hydrolysis-resistant, heat-stabilized PA66 resin. Available in natural, it is specifically designed to maximize the retention of physical properties when exposed to anti-freeze solutions at elevated temperatures. This product is lubricated for improved machine feed and flow.
Glass-reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Vydyne R533H NAT resin is heat-stabilized to minimize oxidative degradation of the polymer when exposed to elevated temperatures in service. This product provides improved retention of physical properties under exposure to long-term heat. Also, Vydyne R533H NAT resin has excellent knit-line strength and fatigue resistance, which is essential for cycle testing with anti-freeze solutions.
Typical Applications/End Uses:
Vydyne R533H NAT resin has been used for many under-the-hood automotive applications, motor housings for power tools and garden appliances. This resin has also been used in miscellaneous brackets, gears and clips that require high rigidity and strength.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHeat StabilizedMold ReleaseHydrolysis ResistanceHigh FlowFilled & Reinforced | |||
| Additive | Heat StabilizerLubricant | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Compliance | EC 2023/2006EU 2011/10/ECFDA | |||
| Reinforced | 33% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Across Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Break | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Conditioned, 23°C |
Break | *** % | ISO 527-2 | Dry, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Conditioned, 23°C |
- | *** Mpa | ISO 178 | Dry, 23°C |
Poisson Ratio | *** - | ISO 527-2 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Dry, Unannealed |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | Dry |
1.5mm | *** °C | IEC 60695-2-12 | Dry |
3mm | *** °C | IEC 60695-2-12 | Dry |
Glow Wire Ignition Test(GWIT) | |||
0.75mm | *** °C | IEC 60695-2-13 | Dry |
1.5mm | *** °C | IEC 60695-2-13 | Dry |
3.0mm | *** °C | IEC 60695-2-13 | Dry |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Dry, 3.00 mm |
Comparative Tracking Index (CTI) | |||
- | ***~*** V | IEC 60112 | Dry, 3.00 mm |
Dielectric Strength | *** kV/mm | IEC 60243 | Dry, 1.00 mm |
Arc Resistance | *** PLC | ASTM D495 | Dry, 3.00 mm |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746 | Dry |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 0.75 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 1.50 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 3.00 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 0.75 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 1.50 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 3.00 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.