R530J BK0723 is a black, 30% glass-filled, high-flow PA66 resin that is heat-stabilized with an electrically neutral heat stabilizer. It is specially designed for electrical applications requiring high dielectric strength, low conductivity and corrosion resistance.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHeat StabilizedGood ColoringLaser MarkableMold ReleaseChemical ResistanceHigh FlowFilled & Reinforced | |||
| Additive | Heat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | Dry |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Across Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Break | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Conditioned, 23°C |
Break | *** % | ISO 527-2 | Dry, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Conditioned, 23°C |
- | *** Mpa | ISO 178 | Dry, 23°C |
Poisson Ratio | *** - | ISO 527-2 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Dry, Unannealed |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
Burning Rate | mm/min | ISO 3795 | Dry, 2.00 mm, Self-Extinguishing |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Dry, 3.00 mm |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | Dry, 3.00 mm |
Dielectric Strength | *** kV/mm | IEC 60243 | Dry, 1.00 mm |
Arc Resistance | *** PLC | ASTM D495 | Dry, 3.00 mm |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746 | Dry |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 0.75 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 1.50 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 3.00 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 0.75 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 1.50 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 3.00 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.