Vydyne R413H NT is general-purpose, heat-stabilized, impact-modified, 15% glass-fiber reinforced PA66 resin. Available in natural, It is specifically designed to maximize toughness, while retaining physical properties. This product is also lubricated for improved flow and offers superior surface appearance.
Glass-fiber reinforced Vydyne resins provide higher heat distortion temperature, resistance to creep and better dimensional stability when compared with unreinforced PA66. These products have good chemical resistance to a broad range of chemicals including gasoline, hydraulic fluids and most solvents.
Typical Applications/End Uses:
Vydyne R413H NT is successfully used in a wide range of injection-molding engineering applications, including automotive clips, fasteners, brackets and carbon canisters; electrical connectors, housings, bobbins, etc.; and industrial gears, bearing shells, covers, housings, etc.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthHigh Stiffness/RigidityHigh ImpactHeat StabilizedDimensional StabilityCreep ResistantMold ReleaseChemical ResistanceFuels ResistantOil ResistantAnti-SolventHigh FlowFilled & Reinforced | |||
| Additive | Impact ModifierHeat StabilizerLubricant | |||
| Appearance | Pellets/GranulesNatural Color | |||
| Processing | Injection | |||
| Reinforced | 15% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Across Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Break | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Conditioned, 23°C |
Break | *** % | ISO 527-2 | Dry, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Conditioned, 23°C |
- | *** Mpa | ISO 178 | Dry, 23°C |
Poisson Ratio | *** - | ISO 527-2 | Dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Conditioned |
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Dry |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180 | Conditioned |
-40℃ (-40℉) | *** kJ/m² | ISO 180 | Dry |
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Dry, Unannealed |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Dry, 0.75 mm |
Comparative Tracking Index (CTI) | |||
- | ***~*** V | IEC 60112 | Dry, 3.00 mm |
Dielectric Strength | *** kV/mm | IEC 60243 | Dry, 1.00 mm |
Arc Resistance | *** PLC | ASTM D495 | Dry, 3.00 mm |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746 | Dry |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 0.40 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 0.75 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 1.50 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 3.00 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | Dry, 0.40 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | Dry, 0.75 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | Dry, 1.50 mm |
High Ampere Arc Ignition(HAI) | *** PLC | UL 746 | Dry, 3.00 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.