Vydyne 47H BK03 is general-purpose, impact-modified PA66 resin. Available in black, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 47H BK03 was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated.
Vydyne 47H BK03 is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline. Vydyne 47H BK03 is designed to meet the critical low-temperature impact requirements called out in many automotive specifications.
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactHigh Impact at Low TemperaturGood ToughnessHeat StabilizedWear/Abrasion ResistanceEasy processingChemical ResistanceFuels ResistantOil ResistantAnti-Solvent | |||
| Additive | Impact ModifierHeat Stabilizer | |||
| Appearance | Pellets/GranulesBlack | |||
| Processing | Injection | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Across Flow | *** % | ISO 294-4 | 23°C, 2.00 mm |
Water Absorption | *** % | ISO 62 | 24 hr, 23°C |
Water Absorption | *** % | ISO 62 | Equilibrium, 23°C, 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Tensile Modulus | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Strength | |||
Yield | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Yield | *** Mpa | ISO 527-2 | Dry, 23°C |
Break | *** Mpa | ISO 527-2 | Conditioned, 23°C |
Break | *** Mpa | ISO 527-2 | Dry, 23°C |
Tensile Elongation | |||
Break | *** % | ISO 527-2 | Conditioned, 23°C |
Break | *** % | ISO 527-2 | Dry, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Conditioned, 23°C |
Flexural Modulus | *** Mpa | ISO 178 | Dry, 23°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | Conditioned, 23°C |
- | *** Mpa | ISO 178 | Dry, 23°C |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Conditioned |
-40℃ (-40℉) | *** kJ/m² | ISO 179 | Dry |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 179 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 179 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 179 | Dry |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180 | Conditioned |
-40℃ (-40℉) | *** kJ/m² | ISO 180 | Dry |
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Conditioned |
-30℃ (-22℉) | *** kJ/m² | ISO 180 | Dry |
23℃ (73℉) | *** kJ/m² | ISO 180 | Conditioned |
23℃ (73℉) | *** kJ/m² | ISO 180 | Dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-2/B | Dry, Unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-2/A | Dry, Unannealed |
Relative Temperature Index(RTI), Imp | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Relative Temperature Index(RTI), Elec | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Relative Temperature Index(RTI), Str | |||
0.75/0.8mm | *** °C | UL 746 | Dry |
1.5/1.6 mm | *** °C | UL 746 | Dry |
3.0/3.2 mm | *** °C | UL 746 | Dry |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Across Flow | *** E-6 cm/cm/℃ | ISO 11359-2 | Dry, 23 to 55°C, 2.00 mm |
Melt Temperature(Tm) | *** °C | ISO 11357-3 | Dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
HB | *** mm | UL94 | Dry |
Glow Wire Flammability Index(GWFI) | |||
0.75mm | *** °C | IEC 60695-2-12 | Dry |
1.5mm | *** °C | IEC 60695-2-12 | Dry |
3mm | *** °C | IEC 60695-2-12 | Dry |
Glow Wire Ignition Test(GWIT) | |||
0.75mm | *** °C | IEC 60695-2-13 | Dry |
1.5mm | *** °C | IEC 60695-2-13 | Dry |
3.0mm | *** °C | IEC 60695-2-13 | Dry |
FMVSS | *** pass | FMVSS 302 | Dry |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | IEC 60093 | Dry, 0.75 mm |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | Dry, 3.00 mm |
Dielectric Strength | *** kV/mm | IEC 60243 | Dry, 1.00 mm |
Arc Resistance | *** PLC | ASTM D495 | Dry, 3.00 mm |
High Voltage Arc Tracking Rate(HVTR) | *** PLC | UL 746 | Dry |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 0.75 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 1.50 mm |
Hot Wire Ignition(HWI) | *** PLC | UL 746 | Dry, 3.00 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 0.75 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 1.50 mm |
High Ampere Arc Ignition(HAI) | PLC | UL 746 | Dry, 3.00 mm |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.