20% Glass Reinforced, High Flow, Halogen free and free of red phosphorous
| Original Document | Technical Datasheet(English) | |||
| Status | Business Restructured | |||
| Features | Flame RetardantHalogen FreeNon Red PhosphorusHigh FlowFilled & Reinforced | |||
| Additive | Flame Retardant | |||
| Processing | Injection | |||
| Reinforced | 20% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | dry |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | dry |
Across Flow | *** % | ISO 294-4 | dry |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | dry |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | dry |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | dry |
Flexural Modulus | *** Mpa | ISO 178 | dry |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | dry |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75-1/-2 | dry |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | dry |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | dry |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | IEC 60695-11-10 | dry |
V-0 | *** mm | IEC 60695-11-10 | dry |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Dielectric Constant(Permittivity) | |||
1 GHz | *** - | IEC 60250 | dry |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | dry |
Dielectric Strength | *** kV/mm | IEC 60243-1 | dry |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.