40% Glass Reinforced, Flame Retardant, Excellent Mold Release, Low Flash, Hydrolysis resistant
| Original Document | Technical Datasheet(English) | |||
| Features | Flame RetardantMold ReleaseLow flashHydrolysis ResistanceFilled & Reinforced | |||
| Processing | Injection | |||
| Reinforced | 40% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Mold Shrinkage | |||
Flow | *** % | ISO 294-4 | |
Across Flow | *** % | ISO 294-4 | |
Moisture /Humidity Absorption | *** % | ISO 62 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 120°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 160°C |
Tensile Modulus | *** Mpa | ISO 527-1/-2 | 200°C |
Tensile Strength | |||
Break | *** Mpa | ISO 527-1/-2 | |
Break | *** Mpa | ISO 527-1/-2 | 120°C |
Break | *** Mpa | ISO 527-1/-2 | 160°C |
Break | *** Mpa | ISO 527-1/-2 | 200°C |
Tensile Elongation | |||
Break | *** % | ISO 527-1/-2 | |
Break | *** % | ISO 527-1/-2 | 120°C |
Break | *** % | ISO 527-1/-2 | 160°C |
Break | *** % | ISO 527-1/-2 | 200°C |
Flexural Modulus | *** Mpa | ISO 178 | |
Flexural Modulus | *** Mpa | ISO 178 | 120°C |
Flexural Modulus | *** Mpa | ISO 178 | 160°C |
Flexural Modulus | *** Mpa | ISO 178 | 200°C |
Flexural Strength | |||
- | *** Mpa | ISO 178 | |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Charpy Notched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eA | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eA | |
Charpy Unnotched Impact Strengh | |||
-30℃ (-22℉) | *** kJ/m² | ISO 179/1eU | |
23℃ (73℉) | *** kJ/m² | ISO 179/1eU | |
Izod Notched Impact Strengh | |||
-40℃ (-40℉) | *** kJ/m² | ISO 180/1A | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | |
Izod Unnotched Impact Strengh | |||
23℃ (73℉) | *** kJ/m² | ISO 180/1U | |
| Hardness | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Rockwell M | *** M | ISO 2039-2 | |
Rockwell R | *** R | ISO 2039-2 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75-1/-2 | |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ISO 11359-1/-2 | |
Flow | *** E-6/°C | ISO 11359-1/-2 | above Tg |
Across Flow | *** E-6/°C | ISO 11359-1/-2 | |
Across Flow | *** E-6/°C | ISO 11359-1/-2 | above Tg |
Melt Temperature(Tm) | *** °C | ISO 11357-1/-3 | 10°C/min |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
V-0 | *** mm | IEC 60695-11-10 | |
V-0 | *** mm | IEC 60695-11-10 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-m | IEC 60093 | |
Dielectric Constant(Permittivity) | |||
5 GHz | *** - | IEC 60250 | |
Dissipation Factor | |||
5 GHz | *** E-4 | IEC 60250 | |
Comparative Tracking Index (CTI) | |||
- | *** V | IEC 60112 | |
Dielectric Strength | *** kV/mm | IEC 60243 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.