30% Glass Reinforced, PA4T, Electro-friendly, for E&E applications
ForTii® JTX2 has robust mechanical performance and has good reliability in thermal ageing and mechanical shocks. JTX2 has consistent performance in injection molding processing and a low risk of blistering due to its JEDEC MLS 1 rating for specified thicknesses. JTX2 is the best candidate for HB reflow headers/connectors in (auto) E&E.
| 原厂资料 | 物性表(英文) | |||
| 产品特性 | 耐热老化填充增强 | |||
| 成型方式 | 注塑 | |||
| 法规认证 | JEDEC MSL(半导体电子元件吸湿等级) | |||
| 增强填充 | 30% 玻纤 | |||
| 物理性能 | 值/单位 | 测试标准 | 测试条件 |
|---|---|---|---|
密度 | 1.43 g/cm³ | ISO 1183 | dry |
收缩率 | |||
纵向(Flow) | 0.4 % | ISO 294-4 | dry |
横向(Across Flow) | 1.2 % | ISO 294-4 | dry |
吸湿率 | 2 % | ISO 62 | dry |
| 机械性能 | 值/单位 | 测试标准 | 测试条件 |
拉伸强度 | |||
断裂(brk) | 180 Mpa | ISO 527-1/-2 | cond. |
断裂(brk) | 200 Mpa | ISO 527-1/-2 | dry |
断裂(brk) | 135 Mpa | ISO 527-1/-2 | dry, 120°C |
断裂(brk) | 90 Mpa | ISO 527-1/-2 | dry, 160°C |
断裂(brk) | 75 Mpa | ISO 527-1/-2 | dry, 200°C |
断裂(brk) | 180 Mpa | ISO 527-1/-2 | dry, 80°C |
拉伸延伸率 | |||
断裂(brk) | 2 % | ISO 527-1/-2 | cond. |
断裂(brk) | 2.1 % | ISO 527-1/-2 | dry |
断裂(brk) | 3.6 % | ISO 527-1/-2 | dry, 120°C |
断裂(brk) | 7 % | ISO 527-1/-2 | dry, 160°C |
断裂(brk) | 8 % | ISO 527-1/-2 | dry, 200°C |
断裂(brk) | 4 % | ISO 527-1/-2 | dry, 80°C |
弯曲强度 | |||
- | 315 Mpa | ISO 178 | dry |
弯曲模量 | 10500 Mpa | ISO 178 | dry |
弯曲模量 | 5000 Mpa | ISO 178 | dry, 160°C |
弯曲模量 | 4000 Mpa | ISO 178 | dry, 200°C |
拉伸模量 | 11000 Mpa | ISO 527-1/-2 | cond. |
拉伸模量 | 11000 Mpa | ISO 527-1/-2 | dry |
拉伸模量 | 7500 Mpa | ISO 527-1/-2 | dry, 120°C |
拉伸模量 | 4500 Mpa | ISO 527-1/-2 | dry, 160°C |
拉伸模量 | 4000 Mpa | ISO 527-1/-2 | dry, 200°C |
拉伸模量 | 10500 Mpa | ISO 527-1/-2 | dry, 80°C |
| 冲击性能 | 值/单位 | 测试标准 | 测试条件 |
简支梁缺口(Charpy Notched) | |||
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | cond. |
23℃ (73℉) | 10 kJ/m² | ISO 179/1eA | dry |
简支梁无缺口(Charpy Unnotched) | |||
23℃ (73℉) | 60 kJ/m² | ISO 179/1eU | cond. |
23℃ (73℉) | 60 kJ/m² | ISO 179/1eU | dry |
| 热学性能 | 值/单位 | 测试标准 | 测试条件 |
热变形温度(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | 305 °C | ISO 75-1/-2 | dry |
线性膨胀系数(CLTE) | |||
纵向(Flow) | 33 E-6/°C | ASTM D 696 | dry |
横向(Across Flow) | 40 E-6/°C | ASTM D 696 | dry |
熔融温度(Tm) | 325 °C | ISO 11357-1/-3 | dry |
温度指数(TI)-拉伸强度 | |||
5000 h | 177 °C | IEC 60216 | dry |
| 燃烧性能 | 值/单位 | 测试标准 | 测试条件 |
UL 防火等级 | |||
HB | 0.4 mm | IEC 60695-11-10 | dry |
HB | 1.5 mm | IEC 60695-11-10 | dry |
| 电学性能 | 值/单位 | 测试标准 | 测试条件 |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | cond. |
体积电阻率 | 1.0E+13 Ohm-m | IEC 60093 | dry |
介电常数(DK) | |||
100Hz | 5 - | IEC 60250 | cond. |
100Hz | 5 - | IEC 60250 | dry |
1MHz | 4.5 - | IEC 60250 | cond. |
1MHz | 4.5 - | IEC 60250 | dry |
1 GHz | 4 - | IEC 60250 | cond. |
1 GHz | 3.9 - | IEC 60250 | dry |
10 GHz | 3.9 - | IEC 60250 | cond. |
10 GHz | 3.8 - | IEC 60250 | dry |
相对漏电起痕指数(CTI ) | |||
- | 600 V | IEC 60112 | dry |
绝缘强度 | 40 kV/mm | IEC 60243-1 | cond. |
绝缘强度 | 43 kV/mm | IEC 60243-1 | dry |