LNP THERMOCOMP AM, grade name EZ006EXAR1, is a compound based on PEI resin containing 30% glass fiber for Large Format Additive manufacturing (LFAM) applications requiring better dimensional stability and low CTE. PEI compounds, based on SABIC's inherently flame-retardant ULTEM(TM) resins, offer high temperature performance, excellent strength-to-weight ratio, high modulus and low creep
| Original Document | Technical Datasheet(English) | |||
| Features | Filled & Reinforced | |||
| Processing | 3D Printing | |||
| Reinforced | 30% Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | XZ Orientation,5mm/min |
Tensile Modulus | *** Mpa | ASTM D638 | ZX Orientation,5mm/min |
Tensile Strength | |||
- | *** Mpa | ASTM D 638 | XZ Orientation,5mm/min |
- | *** Mpa | ASTM D 638 | ZX Orientation,5mm/min |
Tensile Elongation | |||
- | *** % | ASTM D 638 | XZ Orientation,5mm/min |
- | *** % | ASTM D 638 | ZX Orientation,5mm/min |
Flexural Strength | |||
- | *** Mpa | ASTM D790 | XZ Orientation,5mm/min |
- | *** Mpa | ASTM D790 | ZX Orientation,5mm/min |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2mm, annealed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.