LNP* Thermocomp* ZKC06 is a compound based on PPO resin containing Mineral Filler, Impact Modifier. Added features of this material include: high dielectric constant (Dk), extremely low dissipation factor (Df), good ductility, and good thermal performance.
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactGood ToughnessHeat ResistanceFilled & Reinforced | |||
| Additive | Impact Modifier | |||
| Reinforced | 30% Mineral | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Volume Flow Rate(MVR) | |||
300°C/5.0 kg | *** cm³/10 min | ISO 1133 | |
300°C/10.0 kg | *** cm³/10 min | ISO 1133 | |
Melt Mass Flow Rate(MFR) | |||
300°C/5.0 kg | *** g/10 min | ASTM D 1238 | |
300°C/10.0 kg | *** g/10 min | ASTM D 1238 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294 | flow, 24 hrs |
Across Flow | ***~*** % | ISO 294 | xflow, 24 hr |
Water Absorption | *** % | ISO 62-1 | 23°C/24hrs |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Yield | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 50 mm/min |
Yield | *** % | ISO 527 | 50 mm/min |
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ISO 527 | 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Yield | *** Mpa | ISO 178 | 2 mm/min |
Break | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Break | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
-20℃ (-4℉) | *** J/m | ASTM D256 | |
-20℃ (-4℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*4 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
0.45 Mpa (66 psi)（4.6kg/cm²） | *** °C | ISO 75/Bf | Flatw 80*10*4 sp=64mm |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Af | Flatw 80*10*4 sp=64mm |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 150°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 150°C, xflow |
| Flammability | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Flame Rating | |||
HB | ***~*** mm | UL94 | |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Dielectric Constant(Permittivity) | |||
1.1 GHz | *** - | Internal | |
1.9 GHz | *** - | Internal | |
5 GHz | *** - | Internal | |
10 GHz | *** - | Internal | |
Dissipation Factor | |||
1.1 GHz | *** E-4 | Internal | |
1.9 GHz | *** E-4 | Internal | |
5 GHz | *** E-4 | Internal | |
10 GHz | *** E-4 | Internal |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.
| Chinese | English | File Format | Action |
|---|---|---|---|
| 物性表(英文) | Technical Datasheet(English) | Down Load |