LNP THERMOCOMP EF004XXP is a compound based on Polyetherimide resin containing Glass Fiber. Added features of this material include: High modulus, high strength, good dimension stability and good warpage control.
| Original Document | Technical Datasheet(English) | |||
| Features | High StrengthDimensional StabilityLow WarpageFilled & Reinforced | |||
| Reinforced | Glass Fiber | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ASTM D792 | |
Melt Mass Flow Rate(MFR) | |||
337°C/6.7 kg | *** g/10 min | ASTM D 1238 | |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 5 mm/min |
Tensile Elongation | |||
Break | *** % | ASTM D638 | Type I, 5 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.