LNP THERMOCOMP Compound DX11354X is a colorable PC based compound with stable plating and RF performance, colored LDS material solution, good surface and processing window, high impact strength. It is a general purpose product available in internal and external parts for Laser Direct Structuring applications.
| Original Document | Technical Datasheet(English) | |||
| Features | High ImpactGood SurfaceEasy processingMetal PlatingLaser Direct Structuring | |||
| Physical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
|---|---|---|---|
Density/Specific Gravity | *** g/cm³ | ISO 1183 | |
Melt Mass Flow Rate(MFR) | |||
300℃/1.2 kg | *** g/10min | ISO 1133 | |
Mold Shrinkage | |||
Flow | ***~*** % | ISO 294 | flow, 24 hrs |
Across Flow | ***~*** % | ISO 294 | xflow, 24 hrs |
Moisture /Humidity Absorption | *** % | ISO 62 | 23°C / 50% RH |
| Mechanical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Tensile Modulus | *** Mpa | ASTM D638 | 50 mm/min |
Tensile Modulus | *** Mpa | ISO 527 | 1 mm/min |
Tensile Strength | |||
Yield | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Yield | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ISO 527 | 50 mm/min |
Break | *** Mpa | ASTM D638 | Type I, 50 mm/min |
Tensile Elongation | |||
Yield | *** % | ASTM D638 | Type I, 50 mm/min |
Yield | *** % | ISO 527 | 50 mm/min |
Break | *** % | ASTM D638 | Type I, 50 mm/min |
Break | *** % | ISO 527 | 50 mm/min |
Flexural Modulus | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Flexural Modulus | *** Mpa | ISO 178 | 2 mm/min |
Flexural Strength | |||
Yield | *** Mpa | ASTM D790 | 1.3 mm/min, 50 mm span |
Yield | *** Mpa | ISO 178 | 2 mm/min |
| Impact | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Izod Notched Impact Strengh | |||
23℃ (73℉) | *** J/m | ASTM D256 | |
23℃ (73℉) | *** kJ/m² | ISO 180/1A | 80*10*3 |
| Thermal | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Heat Deflection Temperature(HDT) | |||
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ASTM D648 | 3.2 mm, unannealed |
1.8 Mpa (264 psi)（18.6kg/cm²） | *** °C | ISO 75/Ae | Edgew 120*10*4 sp=100mm |
Vicat Softening Temperature(VST) | *** °C | ASTM D1525 | Rate A/50 |
Vicat Softening Temperature(VST) | *** °C | ISO 306 | Rate B/50 |
Coefficient of Linear Thermal Expansion | |||
Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, flow |
Across Flow | *** E-6/°C | ASTM E831 | -40°C to 40°C, xflow |
| Electrical | Value/Unit(Sign in to View) | Test Standard | Test Condition |
Volume Resistivity | *** Ohm-cm | ASTM D257 | |
Surface Resistivity | *** Ohm | ASTM D257 | |
Dielectric Constant(Permittivity) | |||
1 GHz | *** - | ASTM D 150 | |
Dissipation Factor | |||
1 GHz | *** E-4 | ASTM D 150 |
The information presented on this datasheet was acquired by AjiEng.com from the producer of the material. AjiEng.com makes substantial efforts to assure the accuracy of this data. However, AjiEng.com assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.